Peelable seal closure assembly

ABSTRACT

The present invention provides a peelable seal for a multi-chambered container including a first edge and a second edge. At least one of the first edge or second edge includes a stress bearing portion and a non-stress bearing portion.

CROSS-REFERENCE TO RELATED APPLICATIONS

Not Applicable.

FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

Not Applicable.

BACKGROUND OF THE INVENTION

The present invention relates to a container for delivering fluids. Inparticular, it relates to a fluid access assembly for a flowablematerials container wherein a conduit of the assembly has an inletclosed by a peel seal structure. The peel seal is activatable byapplying fluid pressure to the peel seal structure. This assembly can beused in flowable materials containers and has been found particularlyuseful with single chamber and multiple chamber medical solutioncontainers.

Multiple chamber containers having sub-chambers separated by a peelseal, frangible seal or other fluid connecting device are widely used toseparately store two or more components that are mixed inside thecontainer prior to administering the mixed solution to a patient. Thecomponents can be in a powder or liquid form and are typically mixedtogether to form a therapeutic solution. Such solutions can includeintravenous solutions, nutritional solutions, drug solutions, enteralsolutions, parenteral solutions, dialysis solutions, pharmacologicalagents including gene therapy and chemotherapy agents, and many otherfluids that may be administered to a patient.

Due to stability, compatibility, or other concerns, some medicalsolutions have to be stored separately prior to administration to apatient. These solutions may be stored in separate containers, but areoften stored in separate chambers of a single container. The chambersand solutions are often separated by a frangible heat seal. Examples ofsuch containers are disclosed in U.S. Pat. Nos. 5,209,347; 5,176,634;and 4,608,043. These prior art containers have frangible seals to permitthe seal to be broken by hand pressure against the sides of the bag toforce the contents to break the seal and permit mixing between thecomponents. Peelable seals are among the frangible seals used thatpermit the seal to be separated by pulling on opposite sides of thecontainer, or by squeezing the container sidewalls.

The chambered container is typically made from a web of flexiblepolymeric materials. Numerous polymeric films have been developed foruse in such containers, and can be a monolayer structure or a multiplelayer structure. Containers can also have multiple webs where the websare joined along peripheral edges and the planar surface of individualwebs are not necessarily attached to one another. The monolayerstructure can be made from a single polymer, or from a polymer blend.Multiple layer structures can be formed by co-extrusion, extrusionlamination, lamination, or any suitable means. The multiple layerstructures can include layers such as a solution contact layer, ascratch resistant layer, a barrier layer for preventing permeation ofoxygen or water vapor, tie layers, or other layers. Selection of theappropriate film depends on the solution to be contained within thecontainer.

The container is typically formed by placing one or more polymeric filmsheets in registration by their peripheral portions and sealing theouter periphery to form a fluid tight pouch. The peripheral seals arepermanent, and therefore, do not peel. The sheets are sealed by heatsealing, radio frequency sealing, thermal transfer welding, adhesivesealing, solvent bonding, ultrasonic or laser welding.

Blown extrusion is another method used to make the pouch. Blownextrusion is a process that provides a moving tube of extrudate exitingan extrusion die. Air under pressure inflates the tube. Longitudinalends of the tube are sealed to form the pouch.

A peelable seal having a peel strength lower than the peripheral sealcan be formed in the container by various methods such as using a lowerheat sealing temperature than used to form the peripheral seal. Apeelable seal typically has an initial or peak peel force required toinitiate separation of the peelable seal, and a plateau force topropagate the separation. Before steam sterilization, these forces areessentially equal. After the chambered container is filled withsolution, it is typically steam sterilized at a temperature of 121° C.During steam sterilization, stress is applied to the edges of thepeelable seal. When stress is applied to the peelable seal at atemperature above the softening point of the container material duringsterilization, deformation occurs at the seal edge. The deformationreduces stress concentrations at the edge of the seal, increasing thepeak peel force necessary to initiate peeling of the peelable seal.After steam sterilization, the peak peel force can be significantlygreater than the plateau force. This increased peak peel force isdetrimental to use of the multichambered container by making it moredifficult to initiate peeling to open the container. This is especiallytrue for patients using the medical solutions who may be infirmed orelderly and unable to provide the force necessary to initiate peeling.Moreover, the peak peel force is difficult to control, some containersremaining easy to initiate peeling in the peelable seal, while othersbecoming almost impossible to initiate by hand.

SUMMARY OF THE INVENTION

Disclosed herein is a flowable materials conveyance assembly having aconduit having a wall defining a first pathway for conveying flowablematerials and having an inlet to the pathway and an outlet from thepathway; and a multiple layer structure having a first web and a secondweb connected together along an interface proximate the inlet, themultiple layer structure is capable of moving from a sealed position toan activated position in response to materials delivered under pressureto the structure along a second pathway different from the first pathwayto allow flowable materials to enter the inlet.

Also disclosed herein is a closure assembly for a container havingopposing sidewalls defining a chamber therebetween; and a conduit havinga portion extending into the chamber and having a fluid inlet,interfacing portions of the sidewalls are connected together along apeel seal over the inlet to define a closure.

Also disclosed herein is a flowable materials container having a pair ofopposing sidewalls defining a chamber therebetween, interfacing portionsof opposed sidewalls are sealed together along a peel seal to define atleast two separate sub-chambers; and a conduit having a portionextending into the chamber and having a fluid inlet, the fluid inlet isclosed by a portion of the peel seal.

Also disclosed herein is a method for mixing two components separatelystored in sub-chambers of a dual chamber container including the stepsof: (1) providing a fluid container having a first chamber, a secondchamber a peel seal dividing the first chamber from the second chamber,and a fluid access device having a fluid inlet positioned inside thechamber, the fluid inlet being sealed closed by a first portion of thepeel seal; (2) activating a second portion of the peel seal to provide afluid pathway between the first chamber and the second chamber withoutactivating the first portion; and (3) activating the first portion ofthe peel seal to open the fluid inlet.

These and other aspects and attributes of the present invention will bediscussed with reference to the following drawings and accompanyingspecification.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 is a plan view of a multichambered container including a peelableseal;

FIG. 2 is a cross-sectional view taken along lines 2-2 of FIG. 1;

FIG. 3 is a cross-sectional view of a multiple layer structure;

FIG. 4 is a cross-sectional view of another embodiment of a multiplelayer structure;

FIG. 5 is a graph showing typical force vs. displacement curves for apeelable seal before and after sterilization;

FIG. 6 is a cross-sectional view of a peelable seal having a serratededge;

FIG. 7 is an enlarged top view of a peelable seal;

FIG. 8 is a cross-sectional view of a peelable seal;

FIG. 9 is a force vs. displacement graph for a peelable seal;

FIG. 10 is a cross-sectional view of a peelable seal;

FIG. 11 is force vs. displacement graph for the seal of FIG. 10;

FIG. 12 is a cross-sectional view of a peelable seal;

FIG. 13 is a schematic plan view of a peelable seal;

FIG. 14 is a schematic plan view of a peelable seal;

FIG. 15 is a schematic plan view of a peelable seal;

FIG. 16 is a schematic plan view of a peelable seal;

FIG. 17 is a schematic plan view of a peelable seal;

FIG. 18 is a schematic top view of a peelable seal;

FIG. 19 is a schematic view of a three-chamber container with peel sealsseparating the chamber, and an administration port, one end of which isembedded in the peel seal;

FIG. 20 is a schematic view of a peelable seal;

FIG. 21 is a schematic view of a peelable seal;

FIG. 22 is a schematic view of a peelable seal;

FIG. 23 is a plan view of a peel seal having a width that varies alongthe length of the seal;

FIG. 24 is an exploded view of a peel seal having a texture;

FIG. 25 is a cross-sectional view of a closure assembly;

FIG. 26 is a cross-sectional view of a closure assembly;

FIG. 27 is a cross-sectional view of a closure assembly;

FIG. 28 is a perspective view of a container having an administrationport;

FIG. 29 is an exploded isometric view of an administration port;

FIG. 30 is a section view of a cap of the administration port;

FIG. 31 is a sectional view of a user removing a cap of theadministration port;

FIG. 32 is a sectional view of a needle inserted into the port;

FIG. 33 is a plan view of a peel seal container with an access member inan inactivated position;

FIG. 34 is a plan view of a peel seal container with an access member inan activated position;

FIG. 35 is a multiple chamber container with a peel seal conduitseparating two chambers of the container;

FIG. 36 is a layered structure prior to peel initiation;

FIG. 37 is the layered structure during peeling; and

FIG. 38 is the former layered structure now completely delaminated.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is susceptible of embodiments in many differentforms. Preferred embodiments of the invention are disclosed with theunderstanding that the present disclosure is to be considered asexemplifications of the principles of the invention and are not intendedto limit the broad aspects of the invention to the embodimentsillustrated.

FIGS. 1 and 2 show container 10 having a first sidewall 12 and a secondsidewall 14 having a permanent peripheral seal 13 and a closure assembly15. The container has a chamber 16 that is divided into a firstsub-chamber 18 and a second sub-chamber 20 by a peelable seal 22. Theseal 22 extends longitudinally of the container from end seam 24 to endseam 25. The seal is effective in separating components such as twoliquids, a solid and a liquid, two gasses, a gas and a liquid and a gasand a solid.

As best seen in FIG. 2, the closure assembly 15 has a conduit 30 havinga fluid flow path 31, a fluid inlet 32 and a fluid outlet 34. A firstportion 40 of the peelable seal 22 extends over the fluid inlet 32 toseal the conduit from fluid flow either inward to the chamber or outwardfrom the chamber. The first portion 40 of the peel sealable seal maysometimes be referred to as a closure or peelable closure. As will bedescribed in greater detail below, the peelable seal 22 has a peelableseal activation force required to move the seal from a closed or sealedposition to an open or activated position. The peelable seal 22 isdesigned to first activate along a second portion 42 of the peelableseal followed by activation of the first portion 40. The second portion42 is spaced a distance from the first portion 40 to ensure mixing ofthe components of the first and second sub-chambers 18, 20 before theoutlet conduit inlet 32 is open and placed in fluid communication withthe mixed contents. In a preferred form of the invention, the secondportion 42 is generally centrally disposed along the length and widthdimensions of the container.

The closure 40 is capable of blocking fluid traveling in either incomingor outgoing directions through the conduit 30. For single or multiplechamber fluid containers, the peelable seal 22 will block an incoming oroutgoing flow of fluid, until the flow of fluid is pressurized above thepeel seal activation force. Thus, the peelable seal protects againstunwanted ingress or egress of fluids from the container.

The Sidewall Materials and Layer Structures

The container 10 is preferably made principally of flexible polymericmaterials, although the container could include non-polymeric materialssuch as metal foils without departing from the invention. Numerouspolymeric films have been developed for use in containers. Suitablefilms may be of a monolayer structure or a multiple layer structure. Themonolayer structure can be made from a single polymer, or from a polymerblend. The multiple layer structures can include layers such as asolution contact layer, a scratch resistant layer, a barrier layer forpreventing permeation of oxygen or water vapor, tie layers, or otherlayers. It is also contemplated to use more than one web of film for oneor both sidewalls. Selection of the appropriate film depends on thesolution or solutions to be contained within the container. Appropriatepolymeric materials are generally selected from homopolymers andcopolymers of polyolefins, polyamides, polyesters, polybutadiene,styrene and hydrocarbon copolymers, polyimides, polyester-polyethers,polyamide-polyethers to name a few.

The seal layer for a multiple chamber container should display bi-modalbehavior. What is meant by bi-modal behavior is that the material iscapable of forming a permanent seal under one set of sealing ormanufacturing conditions and a peelable seal at a second set of sealingor manufacturing conditions. The seal layer can be a homophase polymer,or a matrix-phase polymer system. Suitable homophase polymers includepolyolefins and more preferably polypropylene and most preferably apropylene and ethylene copolymer as described in EP 0875231, which isincorporated herein by reference.

It is also possible to have a seal layer having wall 12 and 14 ofdiffering materials that are not compatible with one another. U.S.patent application Ser. No. 10/351,004, which is incorporated herein byreference, discloses that containers made from such incompatiblematerial, in some instances, may not readily form permanent seals. Thisproblem can be overcome by wrapping a section of one sidewall over anoutside surface of the opposite sidewall and joined thereto. This methodof sealing is disclosed in U.S. Pat. No. 6,024,220 which is incorporatedherein by reference and made a part hereof.

Suitable matrix-phase polymer systems will have at least two components.The two components can be blended together or can be produced in atwo-stage reactor process. Typically, the two components will havedifferent melting point or glass transition temperatures. In the casewhere one of the components is amorphous, its glass transitiontemperature will be lower than the melting point of the othercomponents. Examples of suitable matrix-phase polymer system includes acomponent of a homopolymer or copolymer of a polyolefin and a secondcomponent of a styrene and hydrocarbon copolymer. Another suitablematrix-phase system includes blends of polyolefins such as polypropylenewith polyethylene, or polypropylene with a high isotactic index(crystalline) with polypropylene with a lower isotactic index(amorphous), or a polypropylene homopolymer with a propylene andα-olefin copolymer.

Suitable polyolefins include homopolymers and copolymers obtained bypolymerizing alpha-olefins containing from 2 to 20 carbon atoms, andmore preferably from 2 to 10 carbons. Therefore, suitable polyolefinsinclude polymers and copolymers of propylene, ethylene, butene-1,pentene-1,4-methyl-1-pentene, hexene-1, heptene-1, octene-1, nonene-1and decene-1. Most preferably the polyolefin is a homopolymer orcopolymer of propylene or a homopolymer or copolymer of polyethylene.

Suitable homopolymers of polypropylene can have a stereochemistry ofamorphous, isotactic, syndiotactic, atactic, hemiisotactic orstereoblock. In one preferred form of the invention, the homopolymer ofpolypropylene is obtained using a single site catalyst.

Suitable copolymers of propylene are obtained by polymerizing apropylene monomer with an α-olefin having from 2 to 20 carbons. In amore preferred form of the invention, the propylene is copolymerizedwith ethylene in an amount by weight from about 1% to about 20%, morepreferably from about 1% to about 10% and most preferably from 2% toabout 5% by weight of the copolymer. The propylene and ethylenecopolymers may be random or block copolymers. The propylene copolymermay also be obtained using a single site catalyst.

It is also possible to use a blend of polypropylene and α-olefincopolymers wherein the propylene copolymers can vary by the number ofcarbons in the α-olefin. For example, the present invention contemplatesblends of propylene and α-olefin copolymers wherein one copolymer has a2 carbon α-olefin and another copolymer has a 4 carbon α-olefin. It isalso possible to use any combination of α-olefins from 2 to 20 carbonsand most preferably from 2 to 8 carbons. Accordingly, the presentinvention contemplates blends of propylene and α-olefin copolymerswherein a first and second α-olefins have the following combination ofcarbon numbers: 2 and 6, 2 and 8, 4 and 6, 4 and 8. It is alsocontemplated using more than 2 polypropylene and α-olefin copolymers inthe blend. Suitable polymers can be obtained using a catalloy procedure.Suitable homopolymers of ethylene include those having a density ofgreater than 0.915 g/cc and includes low density polyethylene (LDPE),medium density polyethylene (MDPE) and high density polyethylene (HDPE).

Suitable copolymers of ethylene are obtained by polymerizing ethylenemonomers with an α-olefin having from 3 to 20 carbons, more preferably3-10 carbons and most preferably from 4 to 8 carbons. It is alsodesirable for the copolymers of ethylene to have a density as measuredby ASTM D-792 of less than about 0.915 g/cc and more preferably lessthan about 0.910 g/cc and even more preferably less than about 0.900g/cc. Such polymers are oftentimes referred to as VLDPE (very lowdensity polyethylene) or ULDPE (ultra low density polyethylene).Preferably the ethylene α-olefin copolymers are produced using a singlesite catalyst and even more preferably a metallocene catalyst systems.Single site catalysts are believed to have a single, sterically andelectronically equivalent catalyst position as opposed to theZiegler-Natta type catalysts which are known to have a mixture ofcatalysts sites. Such single-site catalyzed ethylene α-olefins are soldby Dow under the trade name AFFINITY, DuPont Dow under the trademarkENGAGE®, Eastman Kodak under the trade name MXSTEN, and by Exxon underthe trade name EXACT. These copolymers shall sometimes be referred toherein as m-ULDPE.

Suitable copolymers of ethylene also include ethylene and lower alkylacrylate copolymers, ethylene and lower alkyl substituted alkyl acrylatecopolymers and ethylene vinyl acetate copolymers having a vinyl acetatecontent of from about 8% to about 40% by weight of the copolymer. Theterm “lower alkyl acrylates” refers to comonomers having the formula setforth in Diagram 1:

The R group refers to alkyls having from 1 to 17 carbons. Thus, the term“lower alkyl acrylates” includes but is not limited to methyl acrylate,ethyl acrylate, butyl acrylate and the like.

The term “alkyl substituted alkyl acrylates” refers to comonomers havingthe formula set forth in Diagram 2:

R₁ and R₂ are alkyls having 1-17 carbons and can have the same number ofcarbons or have a different number of carbons. Thus, the term “alkylsubstituted alkyl acrylates” includes but is not limited to methylmethacrylate, ethyl methacrylate, methyl ethacrylate, ethyl ethacrylate,butyl methacrylate, butyl ethacrylate and the like.

Suitable polybutadienes include the 1,2- and 1,4-addition products of1,3-butadiene (these shall collectively be referred to aspolybutadienes). In a more preferred form of the invention, the polymeris a 1,2-addition product of 1,3 butadiene (these shall be referred toas 1,2 polybutadienes). In an even more preferred form of the invention,the polymer of interest is a syndiotactic 1,2-polybutadiene and evenmore preferably a low crystallinity, syndiotactic 1,2 polybutadiene. Ina preferred form of the invention, the low crystallinity, syndiotactic1,2 polybutadiene will have a crystallinity less than 50%, morepreferably less than about 45%, even more preferably less than about40%, even more preferably the crystallinity will be from about 13% toabout 40%, and most preferably from about 15% to about 30%. In apreferred form of the invention, the low crystallinity, syndiotactic 1,2polybutadiene will have a melting point temperature measured inaccordance with ASTM D 3418 from about 70° C. to about 120° C. Suitableresins include those sold by JSR (Japan Synthetic Rubber) under thegrade designations: JSR RB 810, JSR RB 820, and JSR RB 830.

Suitable polyesters include polycondensation products of di-orpolycarboxylic acids and di or poly hydroxy alcohols or alkylene oxides.In a preferred form of the invention, the polyester is a polyesterether. Suitable polyester ethers are obtained from reacting 1,4cyclohexane dimethanol, 1,4 cyclohexane dicarboxylic acid andpolytetramethylene glycol ether and shall be referred to generally asPCCE. Suitable PCCE's are sold by Eastman under the trade name ECDEL.Suitable polyesters further include polyester elastomers which are blockcopolymers of a hard crystalline segment of polybutylene terephthalateand a second segment of a soft (amorphous) polyether glycols. Suchpolyester elastomers are sold by DuPont Chemical Company under the tradename HYTREL®.

Suitable polyamides include those that result from a ring-openingreaction of lactams having from 4-12 carbons. This group of polyamidestherefore includes nylon 6, nylon 10 and nylon 12. Acceptable polyamidesalso include aliphatic polyamides resulting from the condensationreaction of di-amines having a carbon number within a range of 2-13,aliphatic polyamides resulting from a condensation reaction of di-acidshaving a carbon number within a range of 2-13, polyamides resulting fromthe condensation reaction of dimer fatty acids, and amide containingcopolymers. Thus, suitable aliphatic polyamides include, for example,nylon 6,6, nylon 6,10 and dimer fatty acid polyamides.

Suitable styrene and hydrocarbon copolymers include styrene and thevarious substituted styrenes including alkyl substituted styrene andhalogen substituted styrene. The alkyl group can contain from 1 to about6 carbon atoms. Specific examples of substituted styrenes includealpha-methylstyrene, beta-methylstyrene, vinyltoluene, 3-methylstyrene,4-methylstyrene, 4-isopropylstyrene, 2,4-dimethylstyrene,o-chlorostyrene, p-chlorostyrene, o-bromostyrene,2-chloro-4-methylstyrene, etc. Styrene is the most preferred.

The hydrocarbon portion of the styrene and hydrocarbon copolymerincludes conjugated dienes. Conjugated dienes which may be utilized arethose containing from 4 to about 10 carbon atoms and more generally,from 4 to 6 carbon atoms. Examples include 1,3-butadiene,2-methyl-1,3-butadiene (isoprene), 2,3-dimethyl-1,3-butadiene,chloroprene, 1,3-pentadiene, 1,3-hexadiene, etc. Mixtures of theseconjugated dienes also may be used such as mixtures of butadiene andisoprene. The preferred conjugated dienes are isoprene and1,3-butadiene.

The styrene and hydrocarbon copolymers can be block copolymers includingdi-block, tri-block, multi-block, star block and mixtures of the same.Specific examples of diblock copolymers include styrene-butadiene,styrene-isoprene, and the hydrogenated derivatives thereof. Examples oftriblock polymers include styrene-butadiene-styrene,styrene-isoprene-styrene,alpha-methylstyrene-butadiene-alpha-methylstyrene, andalpha-methylstyrene-isoprene-alpha-methylstyrene and hydrogenatedderivatives thereof.

The selective hydrogenation of the above block copolymers may be carriedout by a variety of well known processes including hydrogenation in thepresence of such catalysts as Raney nickel, noble metals such asplatinum, palladium, etc., and soluble transition metal catalysts.Suitable hydrogenation processes which can be used are those wherein thediene-containing polymer or copolymer is dissolved in an inerthydrocarbon diluent such as cyclohexane and hydrogenated by reactionwith hydrogen in the presence of a soluble hydrogenation catalyst. Suchprocedures are described in U.S. Pat. Nos. 3,113,986 and 4,226,952, thedisclosures of which are incorporated herein by reference and made apart hereof.

Particularly useful hydrogenated block copolymers are the hydrogenatedblock copolymers of styrene-isoprene-styrene, such as astyrene-(ethylene/propylene)-styrene block polymer. When apolystyrene-polybutadiene-polystyrene block copolymer is hydrogenated,the resulting product resembles a regular copolymer block of ethyleneand 1-butene (EB). As noted above, when the conjugated diene employed isisoprene, the resulting hydrogenated product resembles a regularcopolymer block of ethylene and propylene (EP). One example of acommercially available selectively hydrogenated copolymer is KRATONG-1652 which is a hydrogenated SBS triblock comprising 30% styrene endblocks and a midblock equivalent is a copolymer of ethylene and 1-butene(EB). This hydrogenated block copolymer is often referred to as SEBS.Other suitable SEBS or SIS copolymers are sold by Kurrarry under thetradename SEPTON® and HYBRAR®. It may also be desirable to use graftmodified styrene and hydrocarbon block copolymers by grafting analpha,beta-unsaturated monocarboxylic or dicarboxylic acid reagent ontothe selectively hydrogenated block copolymers described above.

The block copolymers of the conjugated diene and the vinyl aromaticcompound are grafted with an alpha, beta-unsaturated monocarboxylic ordicarboxylic acid reagent. The carboxylic acid reagents includecarboxylic acids per se and their functional derivatives such asanhydrides, imides, metal salts, esters, etc., which are capable ofbeing grafted onto the selectively hydrogenated block copolymer. Thegrafted polymer will usually contain from about 0.1 to about 20%, andpreferably from about 0.1 to about 10% by weight based on the totalweight of the block copolymer and the carboxylic acid reagent of thegrafted carboxylic acid. Specific examples of useful monobasiccarboxylic acids include acrylic acid, methacrylic acid, cinnamic acid,crotonic acid, acrylic anhydride, sodium acrylate, calcium acrylate andmagnesium acrylate, etc. Examples of dicarboxylic acids and usefulderivatives thereof include maleic acid, maleic anhydride, fumaric acid,mesaconic acid, itaconic acid, citraconic acid, itaconic anhydride,citraconic anhydride, monomethyl maleate, monosodium maleate, etc. Thestyrene and hydrocarbon block copolymer can be modified with an oil suchas the oil modified SEBS sold by the Shell Chemical Company under theproduct designation KRATON G2705.

FIG. 3 shows a multiple layer film 49 having a seal layer 50 anintermediate layer 52 and an external layer 54. Tie layers 56 may beemployed to attach the seal layer 50 to the intermediate layer 52 and toattach the intermediate layer 52 to the external layer 54. In apreferred form of the invention the seal layer is a blend ofpolypropylene, an ethylene a-olefin copolymer and a styrene andhydrocarbon copolymer. In a more preferred form of the invention, thepolypropylene is a polypropylene ethylene copolymer, the ethyleneα-olefin copolymer is a LLDPE having a density of less than 0.915 g/ccand the styrene and hydrocarbon copolymer is a block copolymer andpreferably a tri-block copolymer of styrene-ethylene-butylene-styrene ora blend of an SEBS triblock with an SEBS diblock as a minor component.The relative proportions of the components are preferably from about 55%to 75% of the PP by weight, from 5% to 20% by weight of the LLDPE, andfrom 10% to 20% by weight of the SEBS. The ternary blend of the seallayer is capable of forming a permanent seal and a peel seal at atemperature of from about 123 to 128° C. A permanent seal is achieved atsealing temperatures above 160° C.

The intermediate layer 52 may be selected from any of the polyamides setforth herein and most preferably is a blend of from about 85 to 98%polyamide 6 and from 2 to 15% polyamide 616T.

The external layer 54 is selected from polypropylene polymer, and mostpreferably is a propylene ethylene copolymer with an ethylene content ofless than 6% by weight of the copolymer.

The details of the film 49 are more fully set out in U.S. patentapplication Ser. No. 09/439,826, filed Nov. 12, 1999, which isincorporated in its entirety herein by reference and made a part hereof.

Another suitable film is shown in FIG. 4 having three layers, externallayer 60, intermediate layer 62 and seal layer 64. The external layer isa reactor made polypropylene composition having a first component and asecond component. The first component is a polypropylene homopolymer andis present in an amount by weight of the composition of 40%. The secondcomponent is an ethylene-propylene rubber (ethylene 20% and propylene80%) and is present in an amount by weight of the composition of 60%.Suitable products for the external layer are sold by Mitsubishi ChemicalCompany under the trade name Zelas 7023. Zelas 7023 is the subject ofU.S. Patent Application Publication No. 2001/0034416 A1 which isincorporated herein by reference in its entirety and made a part hereof.

The intermediate layer 62 is a polymer blend of Zelas 7023 70% by weightand 30% by weight of a random copolymer of styrene and butadiene thathas been hydrogenated. Suitable random copolymers of styrene andbutadiene are sold by JSR under the trade name Dynaron 2320 P.

The external layer 64 is a polymer blend of 60% by weight Zelas 7023 and40% by weight of a random copolymer of propylene and ethylene such asthe copolymer sold under the trade name Novatec EG 7C.

The film of FIG. 4 displays bi-modal behavior with peel seals beingformed at sealing temperatures of about 125° C. and permanent seals areobtained at about 160° C.

Other suitable films for this application include those disclosed inU.S. Pat. Nos. 5,849,843; 5,998,019; 6,083,587; 6,297,046; 5,139,831;5,577,369; and U.S. Application No. 2003/0077466 A1 which areincorporated herein in their entirety by reference and made a parthereof.

The container 10 is typically formed by placing one or more polymericfilm sheets forming the first sidewall 12 and second sidewall 14 inregistration by their peripheral portions and sealing their periphery 13to form a fluid tight pouch. The sheets are typically sealed by heatsealing, radio frequency sealing, thermal transfer welding, adhesivesealing, solvent bonding, and ultrasonic or laser welding. Blownextrusion is another method that may be used to make the pouch. Blownextrusion is a process that provides a moving tube of extrudate exitingan extrusion die. Air under pressure inflates the tube. Longitudinalends of the tube are sealed to form the pouch. Blown extrusion onlyrequires seals along two peripheral surfaces, where the single ormultiple sheet registration method requires seals along one, three, orfour peripheral surfaces to form the pouch.

Peelable Seal

The peelable seal 22 is preferably created by heat sealing, but may bemade by any of the above-mentioned sealing or welding methods, or anyother suitable method. The peelable seal 22 is peelable such that it maybe peeled by hand pressure to separate the first sidewall 12 and secondsidewall 14 to allow fluid communication between the first chamber 18and second chamber 20, thereby mixing the components contained in them.The peelable seal 22 is peeled, for example, by gripping the firstsidewall 12 and second sidewall 14 of the container 10, and pulling themapart, or be squeezing or pressing the first sidewall 12 and secondsidewall 14 to force the fluid in chambers 18 and 20 against thepeelable seal 22 with sufficient force to separate the peelable seal 22.The peelable seal 22 is strong enough to withstand external stresseswithout peeling resulting from ordinary squeezing during handling,shipment, or from accidental dropping.

In a preferred form of the invention, the peel seal will have a peelseal activation force that falls within a range of from about 3 N/15 mmto about 30 N/15 mm. The peel seal can have varying peel seal activationforces across it length. In a preferred form of the invention, the peelseal activation force of the first portion 40 of the peel seal will begreater than the second portion 42. This will promote activation of thesecond portion of the peel seal before the first portion to ensuremixing of any components in the chambers before the closure is opened toallow fluid flow through the inlet 32. In a preferred form of theinvention, the peel seal activation force of the first portion 40 of thepeel seal 22 is from about 1 N/15 mm to about 5 N/15 mm higher than thepeel seal activation force of the second portion 42 of the peel seal 22.

It is desirable for the peel seal 22 to be capable of adhesive releaseas opposed to cohesive release. Adhesive release of the peel seal meansthat the first sidewall 12 separates from the second sidewall 14 withoutremoving any significant portion of one wall with the other. The releasegenerates a minimum of particles to prevent or minimize contamination ofthe components of the chamber 16 with residual plastic particles.

The peelable seal 22 has edges 70 and 72. The peelable seal 22 is shownin FIGS. 1 and 14 as extending along the length dimension of thecontainer, but could also extend between lateral edges as shown in FIG.13. Alternatively, the peelable seal 22 may be contained completelywithin the first sidewall 12 and second sidewall 14, and not intersectany part of the peripheral seal 13 (FIG. 16). It is further contemplatedthat the peelable seal 22 can extend from a corner, a lateral edge, or alongitudinal edge, and terminate elsewhere in the container 10 (FIGS. 15and 17). The peelable seal 22 may be located anywhere between the firstsidewall 12 and second sidewall 14 depending on the relative sizes ofthe chambers 18 and 20 desired. The chambers 18 and 20 may be filledwith medical or other components for forming therapeutic solutions,including intravenous solutions, nutritional solutions, drug solutions,enteral solutions, parenteral solutions, dialysis solutions,pharmacological agents including gene therapy and chemotherapy agents,and many other fluids that may be administered to a patient. Thecomponents may be liquid, powder, lyophilized tablet, or other suitableform. The components are introduced into the container 10 and chambers18 and 20 using any conventional means, such as delivering through adedicated access port for each chamber 18 and 20. The edges 70 and 72 ofthe peelable seal 22 abut the fluid in chambers 18 and 20.

Containers are often filled at pressures of up to 60 pounds per squareinch (psi). After being filled with solution, the container 10 istypically sterilized using steam. The sterilization typically occurs ata temperature of 121° C.

FIG. 5 shows typical force vs. displacement graph for a peelable seal 22having straight edges 70 and 72. The x axis of FIG. 5 shows displacementalong the length of the peelable seal 22. The y axis shows forcenecessary to peel the peelable seal 22 at specific points along itslength. Curve 74 is the force vs. displacement curve before steamsterilization. Curve 76 is the force vs. displacement curve after steamsterilization. As can be seen from curve 74 of FIG. 5, a force 77 isnecessary to initiate peeling the peelable seal 22 prior to steamsterilization. This force 77 is the same as a plateau force 78, which isnecessary to propagate peeling after initiation.

As curve 76 shows, after steam sterilization, a peak peel force 80 isrequired to initiate peeling the peelable seal 22. The peak peel force80 is significantly greater than a plateau force 82 necessary topropagate peeling. The peak peel force 80 occurs due to sterilization.Sterilization can cause boiling of the solution in the chambers 18 and20 of the container 10. Boiling can cause expansion of the fluids in thechambers 18 and 20, and thereby further stresses the first sidewall andsecond sidewall 12 and 14 by forcing them apart. When stress is appliedto the peelable seal 22 at a temperature above the softening point ofthe container material, deformation at the seal edges 70 and 72 occurs.Deformation can also occur because of water expansion and/or shrinkageof the container material due to crystallization, or in the case ofstretched container films, stress relaxation. This deformation reducesstress concentration at the seal edges 70 and 72, thereby increasing theforce necessary to break the peelable seal 22 to initiate the peelingprocess. This peak peel force 80 is detrimental to ease of use.Moreover, because of the variable nature of the causes, the peak peelforce 80 is variable and hard to control. Some seals 22 may be too easyto activate, peeling during shipping, ordinary handling, or by dropping.Other seals 22 may become almost impossible to initiate peeling by hand.

The present invention overcomes these problems by reducing the peak peel80 force necessary to initiate peeling at the seal edges 70 and 72. Ithas been found that changing the shape of the seal edges 70 or 72 from astraight edge on at least the portion of the peelable seal 22 wherepeeling is to be initiated accomplishes this. This reduces the length ofthe peelable seal 22 that is subject to stress during exposure to hightemperatures during steam sterilization. Thus, the peak peel force 80occurs only on limited portions of the peelable seal 22.

FIG. 6 shows a cross-sectional view of a peelable seal 90 in accord withan embodiment of the present invention prior to steam sterilization.First sidewall 92 and second sidewall 94 of a container are sealed atthe seal 90. The seal 90 defines chambers 96 and 98 in the container.

FIG. 7 is an enlarged top view of the seal 90 of FIG. 6 before steamsterilization. The seal 90 has a sealed area 100, a first seal edge 102,and a second seal edge 104. The first seal edge 102 and second seal edge104 are serrated, having outer points 106 and angular legs 108 extendingat angles from and between the outer points 106. The legs 108 intersectat inner points 110 thereby connecting with outer points 106. Betweenthe inner points 110 and outer points 106 is a depth 112. Though FIG. 7shows both first seal edge 102 and second seal edge 104 serrated, it iscontemplated that only one or the other of the first seal edge 102 orsecond seal edge 104 may be serrated in accord with the presentinvention (FIG. 18). It also is contemplated that the serrations canoccur over the entire length of the seal 90 or only on selectedsections. It is preferred that the serrations be spaced from theperipheral seal 13 of the container 10 to permit peeling of thepermanent seal 13.

FIG. 8 shows a cross-sectional view of the seal 90 after steamsterilization taken along line 120 of FIG. 7 intersecting inner points110. As shown in FIG. 8, an angular joint 122 between the first sidewall92 and second sidewall 94 occurs at the inner points 110, and ismaintained after steam sterilization.

FIG. 9 is a force vs. displacement graph for the serrated peel seal 90of an embodiment of the present invention. The x axis shows displacementalong the length of the seal 90. The y axis shows the force required topeel the seal 90 at points along the length of the seal 90. Curve 124 isthe force vs. displacement curve before steam sterilization. Aninitiation force 126 is necessary to initiate propagation. This forceincreases essentially linearly to a maximum plateau force 128 topropagate the peeling.

FIG. 9 also shows a curve 130 showing force vs. displacement for theserrated peel seal 90 after steam sterilization. Curve 130 demonstratesthe peak peel force 132. The peak peel force 132 is greater than theinitiation force 126 before sterilization, however, it is less than amaximum propagation force 134 necessary to continue the peeling process.This results in a greater ease of use of the container because lessforce is required initiate the peeling process than with a seal withstraight seal edges.

During sterilization, only the outer points 106 (FIG. 7) are subject tostress and deformation, and not the inner points 110 or angular legs108. The outer points 106 are subject to stress because the film tensionis at a maximum at the outer points 106. Thus, the stress concentrationspresent when the seal 90 is made is reduced only at the outer points106, and not at the angular legs 108 or the inner points 110. Stressconcentration is, therefore, retained at inner points 110.

The outer points 106 define an outer stress bearing zone of the peelableseal 90. The outer points 106 bear the stress caused by steamsterilization. The inner points 110 and angular legs 108 define an innernon-stress bearing zone of the seal 90. Creation of a stress-bearingzone may also be accomplished using other shaped seal edges, such as ascalloped seal edge (FIGS. 20 and 22) or a trapezoidal seal edge (FIG.21), other polygonal or geometric shape.

The stress bearing zone in FIGS. 20 and 22 are the crests 140 of thescallops 142. The non-stress bearing zone includes the troughs 144 andsloping sides 146 of the scallops 142. The stress-bearing zone in FIG.21 is created by the flat portions 150 of the trapezoids 152. Thenon-stress bearing zone includes the inner points 154 and sides 156 ofthe trapezoids 152. The present invention also contemplates other sealedge shapes that create stress bearing zone and a non-stress bearingzone.

In the serrated seal embodiment of FIGS. 6 and 7, the first sidewall 12and second sidewall 14 of the container are separated first at the innerpoints 110. The angular joint at inner points 110 further facilitateseparation of the first sidewall 12 and second sidewall 14. As a result(FIG. 9), the peak peel force 132 is lower than plateau force 134 forpropagating the seal 90, which is the sum of the individual forcesrequired to break the seal 90 at inner points 110, angular legs 108 andouter points 106. Because the outer points 106 are a small lengthcompared to the overall length of the seal 90, the contribution of thepoints 106 is small when compared to that contributed by the innerpoints 110 and legs 108. Hence, the plateau force 134 is reducedcompared to a peelable seal 90 having straight edges 70 and 72. Thisallows for providing varying strengths along the length of the peelseal. Peel seal activation forces are reduced in the areas of theserrations which allow for activating the second portion 42 of the peelseal before the first portion 40 (FIG. 1). It also improves thereproducibility of the peak peel force 132. Yet the seal 90 is strongenough to protect the seal 90 against peeling during normal handling.Likewise for scalloped (FIGS. 20 and 22) and trapezoidal (FIG. 21) sealedges, the sidewalls of the container are initially separated at thenon-stress bearing zone such that the peak peel force is lower than theplateau force.

For the serrated seal edge embodiment of FIG. 7, an important factor inreducing the peak peel force 132 is the depth 112 of the serrations. Thedepth 112 controls the slope of the peel force curve 130 before reachingthe plateau value 134. The depth 112 must be sufficiently great topermit separation between the peak peel force 132 and the plateau force134. The minimum depth for reducing the peak peel force 132 is highlydependent on plateau seal force 134 values, i.e., for lower peak peelforces, a greater depth 112 is necessary. Other factors include,mechanical properties of the materials making the container 10, fillingvolume, filling pressure, and stress occurring during the sterilizationprocess. The greater the volume, the higher the initiation force, andthe higher the filling pressure, the higher the initiation force. Thenumber of serrations per unit length is a factor in determining thereduction of the peak peel force 132. The greater the number ofserrations, the greater the peak peal force 132. A balance must bestruck between peeling force and ability of the seal to withstand normalhandling. Experiments have indicated that symmetrical serrations angledat 90°, outer points 106 spaced 8 mm apart, and a depth 112 of 4 mmachieve an acceptable peak peel force 132. Similarly, for embodimentssuch as the scalloped (FIGS. 20 and 22) or trapezoidal shaped (FIG. 21)seal edges, the depth between the stress-bearing zone and thenon-stress-bearing zone must be controlled to balance peeling force andnormal handling.

In another embodiment, the present invention includes a seal 160. FIG.10 shows a cross-sectional view of the seal 160 before steamsterilization. The seal 160 includes a first seal 162 and a second seal164. The second seal 164 is preferably located at a central portion 166of the first seal 162. The seal 160 separates chambers 18 and 20 of thecontainer 10. The first seal 162 also has a lower peel force than thesecond seal 164. Preferably, the first seal separation force is on theorder of 5 N/15 mm, while the second seal separation force is on theorder of 15 N/15 mm. The seal 160 is created preferably by heat sealingthe first sidewall and second sidewall 12 and 14, and by varying thetemperature along the seal 160, such that the temperature to create seal164 is greater than that for the first seal 162. This causes the firstsidewall and second sidewall 12 and 14 at the second seal 164 to adheretogether more at the second seal 164 than the first seal 162. In turn,this requires a greater force to separate the first sidewall and secondsidewall 12 and 14 at the second seal 164 than the first seal 162. Thefirst seal 162 has a first edge 170 and a second edge 172 that are eachin contact with fluid in chambers 18 and 20.

FIG. 11 shows a force vs. displacement graph for the seal 160. Curve 174shows force vs. displacement before steam sterilization. Curve 176 showsforce vs. displacement after steam sterilization. As FIG. 11demonstrates, the initial peak force 178 of first seal 162 after steamsterilization remains lower than maximum plateau force 180 of the secondseal 164.

When sterilized, deformation will occur at the first and second edges170 and 172. This will increase the peel force at first and second edges170 and 172 of the first seal 162. Thus, even if a peak peel force atfirst and second edges 170 and 172 appears as high as three times theplateau value of the first seal 162, it will remain below the peel sealforce required to separate the second seal 164 in the central portion.Thus, no peak peel force will occur in the second seal 164. The seal 160is created by heat sealing the second seal 164 at a higher temperaturethan the first seal 162.

On a similar principle, an another embodiment shown in FIG. 12, a seal180 has a peeling force gradient along the width of the seal 180. Theseal 180 has first and second edges 182 and 184, and a central portion186 between the first and second edges 182 and 184. The peel force atthe first and second edges 182 and 184 is less, preferably approximatelythree times less, than the peel force at the central portion 186. Aswith seal 160 described above, the seal 180 is created by a heat sealhaving a temperature gradient across its width, greater in the middleand less at the edges. A gradient can be obtained, for instance, by adie having heating elements separated by an insulating material layer,and where the temperature of the central heating element is greater thanat the edges. Thus, when a peak peal force occurs at the edges 182 and184, it remains below the peel force at the central portion 186. Thepeel force at the edges 182 and 184 preferably being approximately 5N/15 mm and at the central portion 186 being approximately 15 N/15 mm.In this manner, even if the edges 182 and 184 of the seal 180 experiencea peel force increase of three times, it is still the same or less thanthat in the central portion 186. Thus, no peak peal force occurs.

It is also possible to vary the peel seal activating force along thelength of the peel seal by varying the width of the seal along itslength as shown in FIG. 23. Wider seal portions 187 will activate athigher forces than thinner sections 188. In the embodiment of FIG. 23,the wider seal portion 187 is positioned proximate the administrationport and the weaker seal portion 188 is positioned distal from theadministration port to ensure that mixing of the contents of thechambers by activating the thin sections 188 occurs prior to activatingthe wider seal portion 187.

It is also possible to vary the peel seal strength by varying thesealing temperature along the length of the peel seal with the strengthof the peel seal increasing with increasing temperature, provided ofcourse the temperature is not so high to damage the film.

In yet another embodiment shown in FIG. 24, the peel seal is createdwith a textured sealing die to create a pattern 189 on the surface ofthe sidewalls along the peel seal. The pattern 189 has individualelements 191. The size, shape, texture and density of the individualelements can impact the strength of the peel seal. The greater theheight or depth of the elements the weaker the peel seal strength. Thehigher the density per unit area of the elements the lower the peel sealstrength. The elements can be protuberances extending from the planarsurface of the sidewall or can be indentations extending from the planarsurface in a direction opposite from the protuberances. The patternshown in FIG. 24 has an increasing density of elements with increasingdistance from the closure assembly. This is to ensure peel sealactivation first occurs at a location remote from the closure assemblyto ensure mixing prior to delivering the mixed contents to the patient.

Closure Assemblies

FIGS. 1 and 2 show closure assembly 15 includes the conduit 30 having aninlet 32 and an outlet 34 with a closure 40. The closure can be openedor activated from fluid pressure in the chamber or can be activated fromproviding fluid under pressure from the outlet 34 to the inlet andthrough the conduit. In a preferred form of the invention, the closurewill be positioned inside the chamber 16 and will be activated by fluidin the chamber. This technique of activating uses fluid flowing along apathway other than the pathway 31 of the conduit.

In a preferred form of the invention (FIG. 25), the conduit is anassembly of a membrane tube 200 concentrically mounted within a porttube 190. The port tube/membrane tube assembly has a portion of the porttube extending into the chamber 16 and a portion of the membrane tubeextending outward of the end seam outside the container 10. Thesidewalls 12, 14 are attached to an outer surface of the port tubetypically by heat sealing.

In a preferred form of the invention, the port tube 190 is amultilayered structure and more preferably has a first layer 192 and asecond layer 194. The first layer 192 should be of a non-PVC containingmaterial that is capable of being sealed to the sidewalls 12, 14 of thecontainer 10, and preferably sealed using radio frequency sealingtechniques, but other techniques such as sonic welding, heat transferinduction sealing and the like could be used without departing from thescope of the present invention. In a preferred form of the invention,the first layer 192 is a polymer blend of: (a) from about 25% to about50% by weight and more preferably from about 30% to about 40% by weight,of the first layer a first polyolefin selected from the group consistingof propylene containing polymers, (b) from about 0% to about 50% byweight, and more preferably from about 5% to 40% by weight, of the firstlayer a second polyolefin of an α-olefin containing polymer or copolymerand more preferably is an ethylene and α-olefin copolymer; (c) fromabout 0% to about 40% by weight, and more preferably from about 10% toabout 40% by weight, of the first layer a radio frequency susceptiblepolymer selected from the group consisting of polyamides, ethyleneacrylic acid copolymers, ethylene methacrylic acid copolymers,polyimides, polyurethanes, polyesters, polyureas, ethylene vinyl acetatecopolymers with a vinyl acetate comonomer content from 18% to 50% byweight of the copolymer, ethylene methyl acrylate copolymers with methylacrylate comonomer content from 18% to 40% by weight of the copolymer,ethylene vinyl alcohol with vinyl alcohol comonomer content from 15% to70% by mole percent of the copolymer; and (d) from about 0% to about 40%by weight, and more preferably from 10% to about 40% by weight, of thefirst layer of a thermoplastic elastomer.

One particularly suitable blend for the port tube 190 first layer 192 isa four component blend having by weight the following components: fromabout 10% to about 40% and more preferably 30% of a dimer fatty acidpolyamide, from about 0% to about 50% and more preferably from about 0%to about 10% of an ultra low density polyethylene, from about 25% toabout 50% and more preferably from about 30% to about 40% of apolypropylene and from about 10% to about 40% and more preferably 30%styrene-ethylene-butylene-styrene block copolymer with maleic anhydridefunctionality.

The second layer 194 of the port tube 190 is of a non-PVC containingmaterial that is capable of being solvent bonded to the membrane tube200. In a preferred form of the invention, the second layer 194 is amultiple component blend of the following components by weight: fromabout 25% to about 55% and more preferably from 33%-52% of athermoplastic elastomer, from about 20% to about 45% and more preferablyfrom about 25% to about 42% of a polyester polyether block copolymer,from about 0% to about 15% and more preferably from about 5% to about12% by weight of the second layer an ethylene copolymerized with vinyllower alkyl esters and preferably vinyl acetate, from about 0% to about10% by weight and more preferably from about 1% to about 5% by weight ofthe second layer of a propylene containing polymer and from about 0% toabout 35% by weight of a polymer selected from the group consisting ofacrylonitrile butadiene styrene (ABS) block copolymer, styrene ethylenebutylene copolymer, styrene acrylonitrile copolymer and cyclic olefin orbridged polycylic olefin containing polymers.

One particularly suitable blend of the second layer 194 of the port tubeis a five-component blend having from about 33% to about 35% SEBS(Kraton 1660), from about 25% to about 29% polyester polyether blockcopolymers (Hytrel), from about 5% to about 9% EVA, from about 1% toabout 3% polypropylene and from about 28% to about 32% ABS.

Another suitable blend of the second layer 194 of the port tube is afour-component blend having from about 48% to about 52% SEBS, from about36% to about 42% polyester polyether block copolymer, from about 8% toabout 12% EVA and from about 1% to about 4% polypropylene.

As shown in the FIG. 25, the first layer 192 has a thickness greaterthan the second layer 194. In a preferred form of the invention thefirst layer will have a thickness of from about 15 mils to about 40 milsand more preferably from about 20 mils to about 30 mils. The secondlayer 194 will have a thickness from about 2 mils to about 12 mils andmore preferably from about 5 mils to about 10 mils.

The membrane tube 200 should be fabricated from a non-PVC containingmaterial and should be capable of being bonded, preferably using solventbonding techniques, to the port tube 190. In a preferred form of theinvention, the membrane tube 200 is a multilayered structure. Themembrane tube 200 has an outer layer 202 and an inner layer 204. Theouter layer 202 is of a material selected from the same materials as setforth for the second layer 194 of the port tube. Likewise, the innerlayer 204 of the membrane tube 200 is selected from the same materialsas the first layer 192 of the port tube 190.

A particularly suitable inner layer of the membrane tube is afour-component blend by weight of the inner layer 204 that slightlyvaries from the most preferred first layer of the port tube. Thecomponents are by weight of the inner layer 204 as follows: 40%polypropylene, 40% ultra-low density polyethylene, 10% polyamide and 10%SEBS. It should be understood, however, that the inner layer 204 of themembrane tube could also be selected from the same components and weightpercentage ranges as set forth above for the first layer of the porttube.

In a preferred form of the invention, the outer layer of the membranetube 200 should have a thickness from about 15 mils to about 35 mils andmore preferably from about 20 mils to about 30 mils. The inner layer 204of the membrane tube 202 should have a thickness from about 2 mils toabout 12 mils and more preferably from about 5 mils to about 10 mils.

FIG. 26 shows an alternate embodiment of the membrane tube having threelayers. In addition to the outer layer 202 and inner layer 204 shown inFIG. 25, FIG. 26 shows an intermediate layer 210 interposedtherebetween. The intermediate layer 210 preferably is a thermoplasticelastomer and more preferably an oil modifiedstyrene-ethylene-butylene-styrene block copolymer sold by the ShellChemical Company under the product designation KRATON G2705. Theintermediate layer 210 can also be a blend of from about 99% to about70% of a thermoplastic elastomer and from about 1% to about 30% of apropylene containing polymer.

In yet another preferred form of the invention (FIG. 27), the port tube190 is a multilayered structure and more preferably has a first layer192 and a second layer 194. The first layer 192 should be of a non-PVCcontaining material that is capable of being sealed to the sidewalls 12and 14 of the container 10. In a preferred form of the invention, thefirst layer 192 is a polymer blend of: (a) from about 25% to about 50%,more preferably from about 30% to about 40%, by weight of the firstlayer a first polyolefin selected from the group consisting ofpolypropylene and polypropylene copolymers, (b) from about 0% to about50%, more preferably from about 5% to about 40%, by weight of the firstlayer a second polyolefin of an α-olefin containing polymer or copolymerand more preferably is an ethylene and α-olefin copolymer; (c) fromabout 0% to about 40%, more preferably from about 10% to about 40% ofthe first layer a radio frequency susceptible polymer selected frompolyamides, ethylene acrylic acid copolymers, ethylene methacrylic acidcopolymers, polyimides, polyurethanes, polyesters, polyureas, ethylenevinyl acetate copolymers with a vinyl acetate comonomer content from 12%to 50% by weight of the copolymer, ethylene methyl acrylate copolymerswith methyl acrylate comonomer content from 12% to 40% by weight of thecopolymer, ethylene vinyl alcohol with vinyl alcohol comonomer contentfrom 12% to 70% by mole percent of the copolymer; and (d) from about 0%to about 40%, more preferably from about 10% to about 40% of athermoplastic elastomer by weight of the first layer.

The second layer 194 of the port tube 190 is of a non-PVC containingmaterial that is capable of being solvent bonded to the membrane tube200. In a preferred form of the invention, the second layer 194 is athermoplastic elastomer or a blend of thermoplastic elastomers in anamount by weight of from about 80% to about 100% and a propylenecontaining polymer from about 0% to about 20% by weight of the secondlayer 194. It is also desirable, but optional, that the second layer 194softens slightly at autoclave temperatures so that when the port tubeand membrane tube assembly is steam sterilized, the port tube moretightly adheres to the membrane tube.

As shown in FIG. 27, the first layer 192 has a thickness greater thanthe second layer 194. In a preferred form of the invention the firstlayer will have a thickness of from about 15 mils to about 40 mils andmore preferably from about 20 mils to about 30 mils. The second layerwill have a thickness from about 2 mils to about 10 mils and morepreferably from about 3 mils to about 7 mils.

The membrane tube 200 should be fabricated from a non-PVC containingmaterial and should be capable of being bonded to the port tube 190,preferably using solvent bonding techniques. Solvent bonding is wellknown in the art. Solvent bonding typically includes applying a solventto a polymeric material to partially dissolve the polymer. While in thisdissolved state the dissolved polymer material is placed in contact witha material, such as another polymer, that the polymeric material is tobe bonded to. Suitable solvents for solvent bonding of the materials ofthe present invention include at least the following solvents:cyclohexane, cyclohexanone, toluene, tetrahydofuran, cumene, xylenes,diethyl benzene, decalin, tetralin and amyl benzene to name a few.

Accordingly, to solvent bond the membrane tube 200 to the port tube 190,a portion of the membrane tube 200 that is to be in contact with theport tube is exposed to the solvent, typically by dipping the relevantportion of the membrane tube into the solvent. Then the membrane tube200 is press-fitted into the port tube where a strong bond is formed.

In a preferred form of the invention, the membrane tube 200 is amultilayered structure having an outer layer 220, a core layer 222 andan inner layer 224. In a preferred form of the invention, the outerlayer 220 is a polymer blend of: (a) from about 0% to about 60%, morepreferably from about 20% to about 55% and most preferably from about30% to about 50%, by weight of the outer layer of a polyolefin and (b)from about 40% to about 100%, more preferably from about 45% to about80% and most preferably from about 50% to about 70%, by weight of theouter layer of a thermoplastic elastomer.

Also, in a preferred form of the invention the core layer 222 is apolymer blend of: (a) from about 35% to about 100%, more preferably fromabout 50% to about 90% and most preferably 70% to about 90%, by weightof the core layer of a thermoplastic elastomer and (b) from about 0% toabout 65%, more preferably from about 10% to about 50% and mostpreferably from about 10% to about 30%, by weight of the core layer of apolyolefin.

Also, in a preferred form of the invention, the inner layer 224 is apolymer blend of: (a) from about 25% to about 55%, more preferably fromabout 25% to about 40%, by weight of the inner layer a polyolefin; (b)from about 0% to about 50%, more preferably from about 0% to about 40%and most preferably 0% to about 20%, by weight of the inner layer apolyolefin selected from α-olefin containing polymers or copolymers andmore preferably is an ethylene and α-olefin copolymer; (c) from about 0%to about 40% by weight, more preferably from about 15% to about 40%, ofthe inner layer a radio frequency susceptible polymer selected frompolyamides, ethylene acrylic acid copolymers, ethylene methacrylic acidcopolymers, polyimides, polyurethanes, polyesters, polyureas, ethylenevinyl acetate copolymers with a vinyl acetate comonomer content from 12%to 50% by weight of the copolymer, ethylene methyl acrylate copolymerswith methyl acrylate comonomer content from 12% to 40% by weight of thecopolymer, ethylene vinyl alcohol with vinyl alcohol comonomer contentfrom 12% to 70% by mole percent of the copolymer; and (d) from about 0%to about 40%, more preferably from about 15% to about 40%, by weight ofthe inner layer of a thermoplastic elastomer.

In a preferred form of the invention the outer layer 220 will have athickness from about 3 mils to about 15 mils and more preferably fromabout 3 mils to about 10 mils. The core layer 222 will have a thicknessfrom about 10 mils to about 35 mils and more preferably from about 10mils to about 30 mils. The inner layer 224 will have a thickness fromabout 3 mils to about 15 mils and more preferably from about 5 mils toabout 10 mils.

Medication Port

FIG. 28 generally illustrates a perspective view of a container 301having a first end 323 and a second end 324. The container 301 may beperipherally sealed and may have a liquid 305 or other solution in aninterior of the container 301. The container 301 may have a port 302having a first end 318 and a second end 319. The container 301 isillustrated in a position as is common in actual use. More specifically,the container 301 may be positioned up-right and may have the medicationport 302 elevated above an administration port 315 in actual use.Additionally, a strap 312 for, for example, a hook may be provided tohang the container 301.

Referring now to FIG. 29, the port 302 may have a housing 303 which mayhave a wall 325. Preferably, the port 302 is a medication port throughwhich a medicament may be added or a solution may be removed from thecontainer 301. The housing 303 and the wall 325 may be constructed from,for example, rubber, plastic or any other material generally known tothose skilled in the art. Additionally, the housing 303 may beconstructed of rigid polypropylene which may reduce risk of a needle 307(FIG. 32) puncturing the wall 325. Further, the housing 303 may beconstructed using gamma-grade materials which are approved to withstandgamma irradiation prior to sterilization as a final stage of themanufacturing process. Gamma-grade materials allow for“pre-sterilization” and reduction in autoclaving exposure time.

As illustrated in FIG. 29, the wall 325 may be circular. The wall 325 ofthe housing 303 may have a first end 326 and a second end 327. Thesecond end 327 of the wall 325 may be integrally formed with the secondend 319 of the medication port 302. Additionally, the first end 326 ofthe wall 325 may be integrally formed with a cap 309 wherein the cap 309may be separated from the first end 326 which will be described infurther detail hereinafter.

The first end 326 of the wall 325 may also have a lip 339 whichprotrudes inward toward a center of the housing 303. The lip 339 may bein contact with a septum 304. The lip 339 may also secure the septum 304within the housing 303 by friction, or, alternatively, the septum 304may be sealed to the lip 339. The lip 339 of the wall 325 may have aninner circumference 347 and an outer circumference 314 as shown in FIG.29.

The wall 325 may have a height 328 and may have a first circumference330 at the first end 326 and a second circumference 332 at the secondend 327. Additionally, the first circumference 330 at the first end 326of the wall 325 may be smaller than the second circumference 332 at thesecond end 327 of the wall 325. The smaller circumference 330 at thefirst end 326 of the wall 325 may result in the wall 325 being tapered.More specifically, a taper 331 may result in the wall 325 tilting inwardtoward the center of the housing 303.

The septum 304 of the medication port 302 may be located within the wall325 of the housing 303. Additionally, the septum 304 may be in contactwith an inner wall 350 of the housing 303 as shown in FIG. 30.

The septum 304 may be constructed from, for example, rubber, plastic orany other material generally known to those skilled in the art.Additionally, the septum 304 may be constructed of a polyisoprenematerial which may allow for the septum 304 to re-seal after puncturingthe septum 304 by, for example, the needle 307.

As illustrated in FIG. 29, the septum 304 may be circular. The septum304 may have a height 335 and may have a first circumference 336 and asecond circumference 337. Additionally, the septum 304 may have a firstend 333 and a second end 334. The first circumference 336 at the firstend 333 of the septum 304 may be smaller than the second circumference337 at the second end 334. The smaller circumference 336 at the firstend 333 may result in the septum 304 being tapered. More specifically, ataper wall 338 may result as shown in FIG. 29 wherein an opening at atop side of the septum 304 is greater than at a center of the septum304.

The first end 333 of the septum 304 may be in contact with the lip 339of the wall 325. The lip 339 may secure the septum 304 in place withinthe housing 303 and may provide a liquid-tight fit between the septum304 and the wall 325 of the housing 303.

The septum 304 may also have a target area 316 which may assist ahealth-care provider or other person with insertion of, for example, theneedle 307 into the septum 304. Of course, a cannula or other object maybe used to pierce-the septum 304. The target area 316 may also becolored, for example, red, to contrast with the color, for example,black, of the housing 303. Use of different colors may result in thetarget area 316 being more visible and/or distinguishable to thehealth-care provider or other person.

As further illustrated in FIG. 29, a recess 321 may be located withinthe target area 316 of the first end 333 of the septum 304. The recess321 may assist the health-care provider or other person by providing areduced resistance location to insert the needle 307 through the septum304. The target area 316 may also have a slit 354 instead of, or inaddition to, the recess 321.

The recess 321 may be formed by an internal wall 308 in the target area316 of the septum 304. More specifically, the wall 308 may have a firstcircumference 351 at the first end 333 of the septum and a secondcircumference 352 at a valley 353 within the septum 304. The firstcircumference 351 at the first end 333 of the septum 304 may be greaterthan the second circumference 352 at the valley 353 in the septum 304.The difference in the circumferences of the internal wall 308 may resultin the internal wall 308 being tapered.

The health-care provider or other person may puncture the septum 304 toestablish fluid communication with the liquid 305 in the container 301.A support ring 317 may support the septum 304 when an object, forexample, the needle, is pressed down upon the septum 304. As illustratedin FIG. 29, the support ring 317 may resemble, for example, a ring.

More specifically, when the health-care provider or other person insertsan object through the septum 304, pressure is created on the septum 304.The support ring 317 may allow pressure to be diverted from the outerperiphery of the septum 304 onto the support ring 317. As a result, theseptum 304 may be able to withstand a greater pressure with the supportring 317 than without the support ring 317. The support ring 317 may beconstructed from, for example, rubber, plastic or any other materialgenerally known to those skilled in the art.

The support ring 317 may be circular and may have a first outercircumference 344, a second outer circumference 349 and an innercircumference 345. Additionally, the support ring 317 may have a firstend 340 and a second end 341. The first outer circumference 344 may beat the first end 340 and a second outer circumference 349 may be at thesecond end 341. The first outer circumference 344 may be greater thanthe second outer circumference 349. As a result, the support ring 317may taper downward. More specifically, the support ring 317 may have ataper 348. The first outer circumference 344 and the second outercircumference 349 of the support ring 317 may be in contact with theinner wall 350 of the housing 303 as shown in FIG. 30.

The support ring 317 may also have a height 342 which may be smallerthan the height 328 of the wall 325. The inner circumference 345 of thesupport ring 317 may form a hollow interior area 343 through which theneedle 307 or other object may extend after piercing the septum 304.

The first end 340 of the support ring 317 may be in contact with thesecond end 334 of the septum 304. Additionally, the second end 341 ofthe support ring 317 may be in contact with a lip 313 on the container301.

The housing 303 may also have a cap 309 that may be constructed from,for example, rubber, plastic or any other material generally known tothose skilled in the art. The cap 309 of the housing 303 may have acover 311 having a circumference 346. The cap 309 may also have a ringhandle 310. As illustrated in FIG. 29, the cover 311 and the ring handle310 may be circular. The ring handle 310 of the cap 309 may have ahollow opening 306 through which a user may insert, for example, afinger or hook.

The cover 311 of the cap 309 may also have a line of separation 320. Theline of separation 320 may be a perforation, a score line or other lineof weakness formed between the cover 311 and the lip 339 of the wall325. The line of separation 320 may be formed at the circumference 346of the cover 311. More specifically, the line of separation 320 mayprovide a circumferential point at which the cover 311 may be removedfrom a remainder of the housing 303.

The cover 311 may be integrally formed with the ring handle 310 by aconnector 322 as generally shown in FIG. 29. The connector 322 may besecured to the cover 311 and the ring handle 310 so that a pulling forcemay break the line of separation 320.

FIG. 30 illustrates an embodiment of the medication port 302 of thepresent invention with the cap 309 secured to the wall 325 of thehousing 303. More specifically, FIG. 30 illustrates the medication port302 prior to removal of the cap 309.

When the cap 309 is on the housing 303, the cap 309 may protect theseptum 304 and may create a sterile environment for the septum 304 bysealing the septum 304 from the surrounding environment. Morespecifically, when the cap 309 is secured to the wall 325 of the housing303, dust, pathogens and other harmful substances may not access theseptum 304 located within the housing 303.

Additionally, when the cap 309 is in the sealed position, the septum 304may be protected from physical damage. The cap 309 may preventaccidental damage that may otherwise occur to the septum 304 if theseptum 304 was unprotected.

FIG. 31 illustrates an embodiment of the present invention with the cap309 of the medication port partially removed. The ring handle 310 of thecap 309 may be lifted by, for example, a finger of a user or a hook.When the user pulls on the ring handle 310, the line of separation 320may break and may allow the user to remove the cap 309. When the cap 309is removed, the septum 304 may be exposed. Upon removal of the cap 309,the septum 304 may be ready for use through penetration of the septum304 by, for example, the needle 307.

FIG. 32 illustrates an embodiment of the medication port 302 of thepresent invention with the cap 309 removed from the wall 325 of thehousing 303. FIG. 32 also illustrates the needle 307 inserted throughthe septum 304 to provide fluid communication with the liquid 305 insidethe interior of the container 301.

The septum 304 may be punctured by the needle 307 or cannula (notshown). The needle 307 or other object may pierce the septum 304 throughthe target area 316 on the septum 304. The needle 307 or other objectmay then pass through the hollow interior 343 of the support ring 317.After the needle or other object is inserted into the container 301,liquid may be added or withdrawn to from the container 301 as may berequired.

Access Member

FIG. 33 shows a peel seal container 400 having an access device 402associated therewith. The access member has a piercing cannula 404defining a fluid pathway 406 therethrough, an activating member 408 tomove the cannula 404 from an inactivated position where the piercingcannula 404 has not punctured a sidewall of the container (FIG. 33) toan activated position (FIG. 34) where the cannula pierces a sidewall ofthe container, a fluid line docking portion 410 and a tubing 412connected to the docking portion 410. A suitable access device 402 isdisclosed in U.S. Patent Docket No. DI-5805, which is incorporated inits entirety herein by reference and made a part hereof.

FIG. 35 shows yet another embodiment of a peel seal container 440 havinga fluid conduit 442 between a first and a second chambers 444, 446. Thefluid conduit 442 has opposed ends having fluid outlets 448 with a peelseal 450 formed from the opposed sidewalls being sealed over the fluidoutlets 448. The top or the bottom chamber can be pressed to open thepeel seal over either of the openings to allow the contents of thechambers to mix.

Using a Dual Chamber Peel Seal Container

FIGS. 36-38 show a sequence of activating a peel seal. FIG. 36 shows alayer structure 230 formed from the first wall having its planar surfacein contact with a planar surface of the second wall to define a fullylaminated state. FIG. 37 shows a portion of the first wall 12 liftingfrom the second wall 14 to define a partially delaminated state.Finally, FIG. 38 shows the wall 12 fully disconnected from the wall 14to define a fully delaminated or open state.

As set forth above (FIG. 1), the first portion 40 of the peelable seal22 has a higher peel seal activation energy than the second portion 42.To activate the container shown in FIG. 1, one need only press on one ofthe sidewalls to apply a fluid pressure to the peel seal 22. Upongenerating sufficient pressure the second portion 42 of the peel sealdelaminates thereby creating a fluid pathway from the first sub-chamber18 to the second sub-chamber 20 thereby allowing the contents to mix.Upon adequate mixing of the components the container is pressed again togenerate sufficient pressure to activate the first portion of the peelseal to open the closure to place the conduit fluid communication withthe contents of the chamber.

The present invention contemplates having a second closure attached tothe assembly that must be punctured or activated to draw fluid from theconduit. Such closures are well known in I.V. containers and CAPDcontainers, and are typically associated with fluid administration sets.

Method for Manufacturing and Filling a Dual Chamber Container

The container 10 is fabricated using standard heat sealing techniques.Separate rolled stock of the sidewall material are fed through packagingmachinery where the sidewalls have peripheral edges placed inregistration. Prior to sealing, the longitudinal end seams, a closureassembly 15 is inserted between the walls 12 and 14 and heat sealed inplace. The peel seal 22 can be formed prior to, during or after formingthe permanent seal and is preferably made using heat conduction sealingtechniques. The welding die for the peel seal may have differenttemperatures and shapes along its length to achieve the desired peelseal.

It should be understood that various changes and modifications to thepresently preferred embodiments described herein will be apparent tothose skilled in the art. Such changes and modifications can be madewithout departing from the spirit and scope of the present invention andwithout diminishing its intended advantages. It is therefore intendedthat such changes and modifications be covered by the appended claims.

1. A flowable materials conveyance assembly comprising: a conduit havinga wall defining a first pathway for conveying flowable materials andhaving an inlet to the pathway and an outlet from the pathway; and amultiple layer structure having a first web and a second web connectedtogether along an interface proximate the inlet, the multiple layerstructure is capable of moving from a sealed position to an activatedposition in response to materials delivered under pressure to thestructure along a second pathway different from the first pathway toallow flowable materials to enter the inlet.
 2. The assembly of claim 1,wherein the multiple layer structure is attached to the conduit.
 3. Theassembly of claim 2, wherein the multiple layer structure has anattaching section and a sealing section, the attaching section havingthe conduit inserted between the first layer and the second layer, andwherein the sealing section has the first web attached to the second webin a fluid tight seal over the inlet.
 4. The assembly of claim 3,wherein the first web is connected to the second web along a peel sealin the sealing section.
 5. The assembly of claim 4, wherein the peelseal allows for adhesive release of the first web from the second web.6. The assembly of claim 1, wherein the first web and the second web arecapable of forming a peel seal and a permanent seal.
 7. The assembly ofclaim 6, wherein the first web comprises a matrix-phase polymer system.8. The assembly of claim 7, wherein the matrix polymer is a polyethylenehomopolymer, an ethylene α-olefin copolymer, a polyethylene copolymer, apolypropylene homopolymer, or a polypropylene copolymer and the phasepolymer is a styrene and hydrocarbon random copolymer, a styrene andhydrocarbon block copolymer, and an ethylene α-olefin copolymer.
 9. Theassembly of claim 4, wherein the first web comprises a homophasepolypropylene.
 10. The assembly of claim 4, wherein the peel seal can beactivated by a force within the range of 3-30 N/15 mm.
 11. A closureassembly for a flowable materials container comprising: a containerhaving opposing sidewalls defining a chamber therebetween; and a conduithaving a portion extending into the chamber and having a fluid inlet,interfacing portions of the sidewalls are connected together along apeel seal over the inlet to define a closure.
 12. The assembly of claim11, wherein the closure is capable of being moved from a closed positionto an open position in response to fluid pressure.
 13. The assembly ofclaim 12, wherein the fluid pressure can be generated by a fluid in thechamber or by a fluid outside the chamber.
 14. The assembly of claim 13,wherein the peel seal divides the chamber into at least twosub-chambers.
 15. The assembly of claim 14, wherein the peel seal has afirst portion proximate the closure having a first peel seal activatingforce and a second portion distal from the closure having a second peelseal activating force wherein the second peel seal activating force isless than the first peel seal activating force.
 16. The assembly ofclaim 15, wherein the difference between the first peel seal activatingforce and the second peel seal activating force is greater than about 1N/15 mm and less than about 5 N/15 mm.
 17. A flowable materialscontainer comprising: a pair of opposing sidewalls defining a chambertherebetween, interfacing portions of opposed sidewalls are sealedtogether along a peel seal to define at least two separate sub-chambers;and a conduit having a portion extending into the chamber and having afluid inlet, the fluid inlet is closed by a portion of the peel seal.18. The container of claim 17, wherein the peel seal is moveable from aclosed position to an activated position.
 19. The container of claim 18,wherein the peel seal is moveable from a closed position to an activatedposition in response to fluid pressure applied to the peel seal.
 20. Thecontainer of claim 19, wherein the peel seal has a first portionproximate the inlet having a first peel seal activating force and asecond portion distal from the closure having a second peel sealactivating force wherein the second peel seal activating force is lessthan the first peel seal activating force.
 21. The container of claim17, wherein the conduit is generally circular in cross-sectional shapeand has an axis that extends in a direction parallel to the peel seal.22. The container wherein the conduit is generally circular incross-sectional shape and has an axis that extends in a directiontransverse to the peel seal to define an angle.
 23. The container ofclaim 22, wherein the angle is an obtuse angle.
 24. The container ofclaim 22, wherein the angle is an acute angle.
 25. The container ofclaim 22, wherein the angle is approximately a right angle.
 26. Thecontainer of claim 17, wherein the peel seal has a length, the peel sealhaving a serrated portion along at least a portion of its length. 27.The container of claim 17, wherein the sidewalls are connected togetheralong a permanent seal about a periphery of the container and the peelseal extends between two points on the periphery.
 28. The container ofclaim 27, wherein the peel seal has a first edge and a second edge, andthe serrated portion is located on one of the first edge or the secondedge.
 29. The container of claim 27, wherein the peel seal has a firstedge and a second edge, and a serrated portion is located on both thefirst edge and the second edge.
 30. The container of claim 17, whereinthe serrated portion is spaced from the periphery.
 31. The container ofclaim 27, wherein the serrated portion includes inner points, outerpoints, angular legs connecting the inner points and outer points, and adepth between the outer points and inner points.
 32. The container ofclaim 27, wherein the first sidewall and second sidewall of thecontainer form an angular joint at the inner points.
 33. A method formixing two components separately stored in sub-chambers of a dualchamber container comprising: providing a fluid container having a firstchamber, a second chamber a peel seal dividing the first chamber fromthe second chamber, and a fluid access device having a fluid inletpositioned inside the chamber, the fluid inlet being sealed closed by afirst portion of the peel seal; activating a second portion of the peelseal to provide a fluid pathway between the first chamber and the secondchamber without activating the first portion; and activating the firstportion of the peel seal to open the fluid inlet.
 34. A multiple chambercontainer comprising: a sidewall defining a fluid chamber, a portion ofthe sidewall being sealed together to divide the fluid chamber into atleast two sub-chambers along a peel seal; and an access member attachedto the sidewall for puncturing the sidewall to provide access to thefluid chamber.